Tygon® Ultra Chemical Resistant Tubing
Formulation 2375

After being immersed in aggressive MEK for 16 hours (plus 4 hours drying time), Tygon® Ultra Chemical Resistant Tubing is still clear and flexible while PVC tubing is completely degraded and rendered useless.

Tygon® Ultra Chemical Resistant Tubing offers an unequaled combination of chemical resistance, clarity and flexibility. Tygon® 2375 replaces 2075.

Tygon® Ultra Chemical Resistant Tubing offers an unequaled combination of chemical resistance, clarity and flexibility. Tygon® Ultra Chemical Resistant Tubing is virtually unaffected by acids, bases, ketones, salts and alcohols, fitting the requirements of many applications from battery acid filling to hazardous material handling. It’s entirely plasticizer-free, eliminating fluid contamination and the premature embrittlement and cracking common with many flexible tubings. Its exceptionally smooth inner surface inhibits particulate buildup and reduces the potential for contamination.

Click for complete size chart
Features/Benefits
  • Resistant to highly aggressive chemicals
  • Plasticizer-free — minimizes risk of fluid contamination
  • Exceptionally smooth inner surface inhibits particulate buildup
  • Low sorption maintains fluid integrity n Contains no chemicals listed in California’s Prop 65
Typical Applications
  • Fine and specialty chemical production
  • Battery acid filling
  • Clean and degreaser transfer systems
  • X-ray processing
  • Paint and solvent production
  • Ink and printing fluid dispensing
  • Hazardous materials handling
  • Power generation sampling and drain lines
Tygon® 2375 Tubing Typical Physical Properties
PropertyASTM MethodValue or Rating
Durometer Hardness - Shore A, 15 sec D2240 75
Color-Clear
Tensile Strength - psi (MPa) (at break) D412 1900 (13.1)
Ultimate Elongation, % D412 850
Tear Resistance - lb-f/inch (kN/m) D1004 240 (42.0)
Specific Gravity D7920.9
Water Absorption, % - 24 hours @ 23ºC D570< 0.01
Compression Set Constant Deflection, % - @ 158ºF (70ºC) for 22 hours D395 - Method B 100
Brittleness by Impact Temp - ºF (ºC) D746 -103 (<-75)
Max Recommended Operating Temp - ºF (ºC)- 130 (54)
Low Temperature Flexibility, ºF (ºC) - -103 (-75)
Tensile Modulus, @ 100% Elongation, psi (MPa)D412 425 (2.9)
Tensile Set,75 % of Ultimate Elongation, %D412 300
Unless otherwise noted, all tests were conducted at room temperature (73ºF).  Values shown were determined on 0.075" thick extruded strip or 0.075" thick molded ASTM plaques or molded ASTM durometer buttons.

 